Preparation of FeCo/Cu Core Shell Magnetic Nanoparticles

Shilabati Hembram, Angshuman Sarkar, Amitava Basu Mallick, Pritam Deb

Abstract


FeCo/Cu core shell structure with FeCo as a core and
copper as the shell has been successfully synthesized by
displacement reaction. The morphology, grain size, lattice strain,
and magnetic properties of all the samples were examined by
using transmission electron microscopy (TEM), X-ray diffraction
(XRD), and vibrating sample magnetometer (VSM). Annealing
temperatures and its effect on magnetic properties of the
FeCo/Cu core shell particles was investigated. A maximum
coercivity (Hc) of 398.84 Oe was recorded for the sample heat
treated in magnetic field. The blocking temperatures (TB) and
squareness (Mr/Ms) of the sample gradually increased due to the
influence of temperature and magnetic field.


Keywords


Core/shell; FeCo alloy; displacement reaction; coercivity; blocking temperature; squareness; TEM; VSM

Full Text:

PDF

References


X. Zhang, B. Wang, X. Xu,“Synthesis and magnetic properties of Cucoated

Fe composite nanoparticles,” Appl. Surf. Science,vol. 256, pp.

–4113, January 2010.

Z. Guo, C. S. S. R. Kumar, L. L. Henry, E. E. Doomes, J. Hormes and E.

J. Podlaha, “Displacement Synthesis of Cu Shells Surrounding Co

Nanoparticles,” J. Electrochem. Soc., vol. 152, pp. D1-D5, November

F. Davar, Z. Fereshteha, M. Salavati-Niasari, “Nanoparticles Ni and

NiO: Synthesis, characterization and magnetic properties,”, J. Alloy. and

Compond, vol. 476, pp 797–801, November 2009.

R. Ali, A. Mahmood, M. A. Khan, A. H. Chughtai, M. Shahid, I. Shakir,

M. F. Warsi, “Impacts of Ni–Co substitution on the structural, magnetic

and dielectric properties of magnesium nano-ferrites fabricated by

micro-emulsion method,”, J. Alloy. and Compond, vol. 584, pp 363–

, September 2014.

N.J. Tanga, W. Zhonga, H.Y. Jianga, Z.D. Hana, W.Q. Zoua, Y.W. Dua,

“Complex permeability of FeNi3/SiO2 core-shell nanoparticles,” Sol.

Stat. Communications, vol. 132, pp. 71–74, July 2004.

C. Wanga, R. Lva, Z. Huanga, F.Kanga, J. Gua, “Synthesis and

microwave absorbing properties of FeCo alloy particles/graphite

nanoflake composites,” J. Alloy. Compounds, vol. 509, pp. 494–498,

September 2011.

F. Qiu, Y. Dai, L. Li, C. Xu, Y. Huang,C. Chen, Y. Wang, L. Jiao, H.

Yuan “Synthesis of Cu@FeCo coreeshell nanoparticles for the catalytic

hydrolysis of ammonia borane,” Int. J. Hyd. Energy, vol. 39, pp. 436-

, November 2014.

A. Hutten,D. Sudfelda, I. Ennena, G. Reissa, K. Wojczykowski, P. Jutzi

“Ferromagnetic FeCo nanoparticles for biotechnology,” J. Mag. Mag.

Materials, vol. 293, pp. 93–101, March 2005.

M. Mchenry et al, “Nanocrystalline materials for high temperature soft

magnetic applications: A current prospectus,” Bull. Mater. Sci., vol. 22,

pp. 495-501, May 1999.

G. Han, J. Lu,Y.Gao, “FeCo nanowires deposited in a magnetic field,” J.

Mag. Mag. Materials, vol. 393, pp.199–203, May 2015

T. P. Braga, D. F. Dias, M. F. Sousa, J. M. Soares, J. M. Sasaki,

“Synthesis of air stable FeCo alloy nanocrystallite by proteic sol–gel

method using a rotary oven,” J. Alloy. and Compond, vol. 622, pp 408–

, October 2015.

A. G. Kolhatkar, I. Nekrashevich, D. Litvinov, R. C. Willson, and T. R.

Lee, “Cubic Silica-Coated and Amine-Functionalized FeCo

Nanoparticles with High Saturation Magnetization,” Chem. Materials,

vol. 25, pp. 1092−1097,March 2013.

T. L.Kline,Y. H. Xu,Y.Jing, J. P. Wang, “Biocompatible high-moment

FeCo-Au magnetic nanoparticles for magnetic hyperthermia treatment

optimization,” J. Mag. Mag. Materials, vol. 321, pp. 1525–1528,

February 2009.

T. A. Lafford, M. R. J. Gibbs, C. Shearwood, “Magnetic,

magnetostrictive and structural properties of iron-cobalt/silver

multilayers,” J. Mag. Mag. Materials, vol. 132, pp. 89–94, August 1994.

S. Behrens, H. Bönnemann, N. Matoussevitch, A. Gorschinski, E.

Dinjus, W. Habicht, J. Bolle, S. Zinoveva, N. Palina, J. Hormes, H.

Modrow, S. Bahr and V. Kempter, “Surface engineering of Co and FeCo

nanoparticles for biomedical application,” J. Phy.: Cond. Matter, vol. 18,

pp. s2543. September, 2006.

T. H. D. Keijser, J. I. Langford, E. J. Mittemeijer, A. B. PVogels, “Use

of the Voigt function in a single-line method for the analysis of X-ray

diffraction line broadening,” J.Appl. Cryst, vol. 15, pp. 308-314, June


Refbacks

  • There are currently no refbacks.